Productos de aleacion de titanio
Plates, belts, foils, tubes, rods, forgings, wire titanium alloy products, different types of titanium alloy properties, advantages and disadvantages vary, can be used for different purposes.
TC1
Performance Analysis: MGood stamping. Various types of welding can be performed, and the weldability is good. Machinability is the same as industrial pure titanium. Good oxidation resistance
Working environment: Parts that work below 400°C. Suitable for all kinds of plates, stamping and welding parts
TC2
Performance Analysis: At 350°C, the 100h endurance strength is above 400MPa, and there is good plasticity in hot working. Heated to 350-400 °C, no brittle tendency, therefore, can be used to weld parts that work at high temperatures.
Working Environment: Parts, Weldments, Die Forgings, and Bending Parts that work below 500°C
TC4
Performance analysis: poor stamping, good thermoplasticity. Various types of welding can be performed, and the strength of the welded joint can reach 90% of the base metal strength. Mechanical processing performance is still good, need to use carbide, a large amount of knife, slow speed, adequate cooling. Good corrosion resistance and good thermal stability. It is one of the most widely used titanium alloys.
Working environment: Long-term working parts below 400°C
TC5
Análisis de rendimiento: estable por debajo de 350, caída de plástico a temperaturas más altas. En el estado caliente para forjar, estampado y otras deformaciones
Ambiente de trabajo: piezas trabajando a menos de 350 ° C
TC9
Análisis de rendimiento: la termoplasticidad sigue siendo buena. La maquinabilidad es la misma que la de la aleación T. Alta resistencia a la corrosión La estabilidad térmica sigue siendo buena
Entorno de trabajo: piezas de trabajo de larga duración por debajo de 400 ° C. Puede fabricar placas de compresor y cuchillas
TC10
Análisis de rendimiento: estampado pobre, buena termoplasticidad. Se pueden realizar varios tipos de soldadura, y la resistencia de la unión soldada puede alcanzar el 90% de la resistencia del metal base. El rendimiento de mecanizado es el mismo que el de la aleación T. Buena resistencia a la corrosión. La estabilidad térmica es buena, el efecto del tratamiento térmico es notable y la templabilidad es buena.
Ambiente de trabajo: hacer un trabajo a largo plazo por debajo de 450 ° C
TA6
Análisis de rendimiento:
Tiene un buen rendimiento de soldadura, alta resistencia a la fluencia, pero baja plasticidad de proceso, Deformable en condiciones de calor, la aleación no es sensible al corte cuando se somete a carga axial, y el rendimiento de corte sigue siendo bueno
Entorno de trabajo: piezas y piezas de soldadura que trabajan por debajo de 400 ° C
TA7
Análisis de rendimiento: bajo rendimiento de estampado, la termoplasticidad sigue siendo buena. Se pueden realizar diversas formas de soldadura con un buen rendimiento. La resistencia y la plasticidad de la unión soldada pueden ser iguales a las del metal base. El rendimiento del procesamiento mecánico es el mismo que el del titanio puro industrial. Buena resistencia a la corrosión, buena estabilidad térmica a alta temperatura
Ambiente de trabajo: hacer trabajo estructural para trabajos a largo plazo por debajo de 500 ° C, puede hacer varias piezas forjadas
TA8
Análisis de rendimiento: buena termoplasticidad. Se pueden realizar varios tipos de soldadura y la soldabilidad es buena. La maquinabilidad es lo mismo que el titanio puro industrial. Buena resistencia a la oxidación
Entorno de trabajo: piezas de trabajo de larga duración por debajo de 500 ° C. Puede hacer las placas y las cuchillas del compresor del motor
TC1
Performance Analysis: MGood stamping. Various types of welding can be performed, and the weldability is good. Machinability is the same as industrial pure titanium. Good oxidation resistance
Working environment: Parts that work below 400°C. Suitable for all kinds of plates, stamping and welding parts
TC2
Performance Analysis: At 350°C, the 100h endurance strength is above 400MPa, and there is good plasticity in hot working. Heated to 350-400 °C, no brittle tendency, therefore, can be used to weld parts that work at high temperatures.
Working Environment: Parts, Weldments, Die Forgings, and Bending Parts that work below 500°C
TC4
Performance analysis: poor stamping, good thermoplasticity. Various types of welding can be performed, and the strength of the welded joint can reach 90% of the base metal strength. Mechanical processing performance is still good, need to use carbide, a large amount of knife, slow speed, adequate cooling. Good corrosion resistance and good thermal stability. It is one of the most widely used titanium alloys.
Working environment: Long-term working parts below 400°C
TC5
Análisis de rendimiento: estable por debajo de 350, caída de plástico a temperaturas más altas. En el estado caliente para forjar, estampado y otras deformaciones
Ambiente de trabajo: piezas trabajando a menos de 350 ° C
TC9
Análisis de rendimiento: la termoplasticidad sigue siendo buena. La maquinabilidad es la misma que la de la aleación T. Alta resistencia a la corrosión La estabilidad térmica sigue siendo buena
Entorno de trabajo: piezas de trabajo de larga duración por debajo de 400 ° C. Puede fabricar placas de compresor y cuchillas
TC10
Análisis de rendimiento: estampado pobre, buena termoplasticidad. Se pueden realizar varios tipos de soldadura, y la resistencia de la unión soldada puede alcanzar el 90% de la resistencia del metal base. El rendimiento de mecanizado es el mismo que el de la aleación T. Buena resistencia a la corrosión. La estabilidad térmica es buena, el efecto del tratamiento térmico es notable y la templabilidad es buena.
Ambiente de trabajo: hacer un trabajo a largo plazo por debajo de 450 ° C
TA6
Análisis de rendimiento:
Tiene un buen rendimiento de soldadura, alta resistencia a la fluencia, pero baja plasticidad de proceso, Deformable en condiciones de calor, la aleación no es sensible al corte cuando se somete a carga axial, y el rendimiento de corte sigue siendo bueno
Entorno de trabajo: piezas y piezas de soldadura que trabajan por debajo de 400 ° C
TA7
Análisis de rendimiento: bajo rendimiento de estampado, la termoplasticidad sigue siendo buena. Se pueden realizar diversas formas de soldadura con un buen rendimiento. La resistencia y la plasticidad de la unión soldada pueden ser iguales a las del metal base. El rendimiento del procesamiento mecánico es el mismo que el del titanio puro industrial. Buena resistencia a la corrosión, buena estabilidad térmica a alta temperatura
Ambiente de trabajo: hacer trabajo estructural para trabajos a largo plazo por debajo de 500 ° C, puede hacer varias piezas forjadas
TA8
Análisis de rendimiento: buena termoplasticidad. Se pueden realizar varios tipos de soldadura y la soldabilidad es buena. La maquinabilidad es lo mismo que el titanio puro industrial. Buena resistencia a la oxidación
Entorno de trabajo: piezas de trabajo de larga duración por debajo de 500 ° C. Puede hacer las placas y las cuchillas del compresor del motor